Cellular Glass Board Insulation can withstand loads which crush most other insulating materials. In a properly designed piping system, it eliminates the need for special treatment at pipe cradles. It provides a fire base for roof membranes, jacketing or vapor retarders, and can prolong their life.
Features
1. Low density, low thermal conductivity and high compressive strength;
2. No water absorption, moisture permeability and leakage;
3. Small thermal expansion coefficient, good dimensional stability, no deformation and no cracking;
4. Fire protection, non combustion and corrosion resistance;
5. No mildew, no mouse sniffing, pest control and microorganism;
6. It is suitable for all kinds of harsh environments such as high temperature, deep cold, constant temperature and humidity.
7. Easy to cut, process and construct;
8. Inorganic products, no aging, no degradation of performance, service life synchronous with buildings;
9. Recycling, innocuity, safety and environmental protection.
Performance Index
| Item | Performance Index | Test Mode | ||||
| I | II | III | IV | |||
| Volume density Kg/m3 | ≤120 | ≤140 | ≤160 | ≤180 | JC/T 647 | |
| Density range | ＞100 ≤120 | ＞120 ≤140 | ＞140 ≤160 | ＞160 ≤180 | ||
| Conductivity W/(m*k) | ≤0.042 | ≤0.045 | ≤0.058 | ≤0.062 | GB/T 10294 | |
| Compressive strength (MPa) | ≥0.5 | ≥0.6 | ≥0.6 | ≥0.7 | GB/T 5486 | |
| Flexural strength (MPa) | ≥0.3 | ≥0.5 | ≥0.5 | ≥0.6 | ||
| Tensile strength vertical to the plane(MPa) | ≥0.15 | JG149 | ||||
| Water Absorption by Vol. (v/v),% | ≤0.5 | JC/T 647 | ||||
| Dimensional stability % | ≤0.3 | GB/T 8811 | ||||
| Combustibility | A1 | GB 8624 | ||||
| Radionuclide limit | internal exposure index(Ira) | ≤1.0 | GB 6566 | |||
| external exposure index(Ir) | ≤1.0 | |||||
| Property | Unit | Grade 800 | Grade 1000 | Grade 1200 | Grade 1600 | ||||
| Ave. Density | kg/m3 | 120±8 | 130±8 | 140±8 | 160±10 | ||||
| Thermal Conductivity | Ave. Value | W/(m·K) | 0.043 | 0.044 | 0.046 | 0.048 | |||
| Highest Single Value | (10℃) | 0.045 | 0.046 | 0.048 | 0.05 | ||||
| Compressive Strength | Ave. Value | MPa | 0.8 | 1 | 1.2 | 1.6 | |||
| Lowest Single Value | 0.55 | 0.69 | 0.83 | 1.1 | |||||
| Water Absorption by Vol. | % | ≤0.5 | |||||||
| Thermal Expansion Coefficient | 1/℃ | 9×10-6 | |||||||
| Service Temp. | ℃ | -196～+450 | |||||||
| Property | Unit | Grade 500 | Grade 700 | Grade 1400 | Grade 2400 | ||||
| Ave. Density | kg/m3 | 110±8 | 115±8 | 150±10 | 220±20 | ||||
| Thermal Conductivity | Ave. Value | W/(m·K) | 0.038 | 0.04 | 0.047 | 0.056 | |||
| Highest Single Value | (10℃) | 0.04 | 0.042 | 0.049 | 0.058 | ||||
| Compressive Strength | Ave. Value | MPa | 0.5 | 0.7 | 1.4 | 2.4 | |||
| Lowest Single Value | 0.35 | 0.48 | 0.97 | 1.66 | |||||
| Water Absorption by Vol. | % | ≤0.5 | |||||||
| Thermal Expansion Coefficient | 1/℃ | 9×10-6 | |||||||
| Service Temp. | ℃ | -196～+450 | |||||||
Application
As an advanced thermal insulation material, cellular glass is widely used in petroleum industry, chemical industry, underground engineering, shipbuilding and defense works. It can be used in the cryogenic insulation system in pharmacy, the cryogenic system in hydrocarbon processing, the low temperature piping, equipment and storage tank, the cold storage and cold storage building, the steel liquid oxygen, liquid nitrogen storage tank and pipeline, and rxterior wall insulation, exterior insulation, roofing, basement.
Flow of Production